| RoHSII : | The material is in compliance with EU directive 2011/65/EU (RoHS II) | Base material : | Woven cotton cloth |
|---|---|---|---|
| Matrix resin : | Phenolic |
Color : | Brown |
| Mechanical Properties | Variant | TestMethod | Value | Unit |
|---|---|---|---|---|
| Flexural stress at rupture perpendicular to laminations | min | ISO 178 | 129 |
MPa |
| Apparent modulus of elasticity in flexure | min | ISO 178 | 6902 |
MPa |
| Compressive strength perpendicular to laminations | min | ISO 604 | 290,94 |
MPa |
| Impact strength (Charpy) parallel to laminations | min | ISO 179/3C | 22,46 |
kJ/m2 |
| Shearing strength parallel | min | VDE 0318/2 | 52,83 |
MPa |
| Tensile strength | min | ISO 527-4 | 92,48 |
MPa |
| Electrical Properties | ||||
| Electric strengthat 90°C in oil perpendicular to laminations | min | IEC 60243-1 | 1,66** |
kV/mm |
| Breakdown voltage at 90°C in oil parallel to laminations | min | IEC 60243-1 | 5
|
kV |
| Insulation resistance after immersion in water | min | IEC 60167 | 20,1 |
M Ω |
| Comparative tracking index CTI | min | IEC 60112 | 150 |
CTI |
| Thermal Properties | ||||
| Thermal endurance | IEC 60216 | 120* |
T.I. | |
| Density | ISO 1183 | 1,372 |
g/cm3 | |
| Water absorption | max | ISO 62 | 207,8* |
mg |
| Fire behaviour and fire side effects | DIN 5510 T.2 | S4;SR2;ST2 |
||
| Smoke gas toxicity | DIN 5510 An.C | 0,21 |
FED | |
| Note: | * for test specimens 50 x 50 x 10mm ** for thickness >=3,0mm Test values are derived from an average type test |